IPDB › China Industry › Metallurgy, Mineral & Energy
China, Chinese Ramming Paste Cold-Ramming Paste Low-Contracting Masses for Aluminum Electrolyers1 Industrial Products Supplier Manufacturer Details, price list catalog:
China Industrial Products Supplier Manufacturer List Catalog
Graphite ProductsCarbon GraphiteCold Ramming PasteElectrode Paste
Hebei Xingshi New Material Technology Co., Ltd
Preview:
Product Description Anthracite Materia Cold Ramming Paste For Ironmaking Blast Furnace Products description :Cold ramming paste refers to a cathode paste that can be laid at room temperature. It is a carbon-filled raw material for masonry. It is widely used in industrial furnaces such as aluminum reduction cells, iron-making blast furnaces, smelting furnaces, and calcium carbide furnaces. The aggregate of this cathode paste is the same as that of ordinary cathode paste (also called hot stamping paste), such as ordinary calcined anthracite or electric calcined anthracite, metallurgical coke, graphite crushing, etc. The low softening point of the adhesive is 20 oC ± 5 oC.According to the softening point of the binder and the construction temperature, the cathode paste can be divided into hot paste, medium temperature paste and cold paste. The application temperature of cold paste is 8 oC ~ 25 oC, the application temperature of medium temperature paste is about 50 oC, and the application temperature of hot paste is over 100 oC. According to the particle size of the aggregate and the size of the filling gap, it can be divided into thick paste and fine paste. The thin seam paste is used to bond the carbon seam of less than 2mm, and its aggregate is mainly coke powder of less than 100 mesh. The thick seam paste is used to fill larger gaps and to smash the carbon pad. Press the use part. Cathode paste can be divided into peripheral paste (peripheral paste), carbon paste, and steel rod paste. According to the different aggregates used, it can be divided into semi-graphite cathode paste and ordinary cathode paste. The semi-graphite cathode paste is used in conjunction with the semi-graphite cathode carbon block, and the ordinary paste is used in conjunction with the ordinary carbon block.OrCold-ramming low-contracting masses are used for ramming interblock and peripheral joints of aluminum electrolyzers at temperatures of 25±10°C. In combination with the base block, the mass ensures the uniformity of the bottom lining in the electrolyzer. The composition of the mass guarantees the uniformity of all physical-chemical processes of baking and a low degree of expansion and contraction. Cold-ramming mass propertiesPROPERTIESVALUEApparent density of unbaked mass, g/cm31,50-1,65Apparent density of baked mass, g/cm31,38-1,50Compressive strength, MPa, min.10-25*Open porosity of baked mass, %21Volume expansion, %0-2,5Degree of compaction, %55-75Contraction rating, max, %0,3Electrical resistivity, max, μm90Ash content, %, max, %3,5* the values difference between two mass batches shall not exceed 10 MPa. Choose a Model as your Construction environment and your Local Enviornmental .If you also need any suggestion , we can provide some profile for you . We finished many factoies workshop .Welcome your inquiry . - Xingshi CarbonWe are professional- to be your trusted partner.
Purchasing Request
Note: Send your purchase request, and we will screen suppliers or manufacturers for you free of charge...