IPDB › China Industry › Metallurgy, Mineral & Energy
China, Chinese Aluminum H20 and Aluminum Alloy H20 Sheet or Plate1 Industrial Products Supplier Manufacturer Details, price list catalog:
China Industrial Products Supplier Manufacturer List Catalog
AluminumAluminum SheetA96061 Aluminum BarA96061 Aluminium Rod
Wuxi Taixie Metal Material Co., Ltd.
Preview:
Product Description [aluminium alloy A96061/A1Mg1SiC /3.3214/H20 ] Introduction:6061 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. 6061 is the Aluminum Association (AA) designation for this material. In European standards, it will be given as EN AW-6061. AlMg1SiCu is the EN chemical designation. H20 is the British Standard (BS) designation. A96061 is the UNS number. Additionally, the AFNOR (French) designation is A-G1SUC. Older literature may refer to this material as CSA GS11N, but this is now discouraged.It has been in use since 1935, but has only received its standard designation in 1954. This material is well established: the Further Reading section below cites a number of published standards, and that list is not necessarily exhaustive.Aluminum 6061 is one of the most versatile of the heat treatable alloy group. Alloy 6061 has good corrosion resistance and good weldability.Aluminum 6061 is probably the most commonly available, heat treatable aluminum alloy.[aluminium alloy A96061/A1Mg1SiC /3.3214/H20 ] Application:Aluminium / Aluminum 6061 alloy is used in the following applications:Truck and marine componentsFurnitureGeneral structural and high pressure applicationsPipelinesHeavy-duty structuresRailroad carsTank fittingsAluminum 6061 is typically used in structural and transportation applications.Aluminum 6061 is commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, and in pipelines.[aluminium alloy A96061/A1Mg1SiC /3.3214/H20 ] Chemistry:Chemical CompositionThe following table shows the chemical composition of Aluminium / Aluminum 6061 alloy.ElementContent (%)Aluminium / Aluminum, Al97.9Magnesium, Mg1Silicon, Si0.60Copper, Cu0.28Chromium, Cr0.20Physical PropertiesThe physical properties of Aluminium / Aluminum 6061 alloy are outlined in the following table.PropertiesMetricImperialDensity2.7 g/cm30.0975 lb/in3Melting point588°C1090°FMechanical PropertiesThe mechanical properties of Aluminium / Aluminum 6061 alloy are tabulated below.PropertiesMetricImperialTensile strength115 MPa16680 psiYield strength48 MPa6962 psiShear strength83 MPa12038 psiFatigue strength62 MPa8992 psiElastic modulus70-80 GPa10153-11603 ksiPoisson's ratio0.330.33Elongation25%25%Hardness3030Thermal PropertiesThe thermal properties of Aluminium / Aluminum 6061 alloy are given in the following table.PropertiesConditionsT (oC)TreatmentThermal expansion co-efficient23.4 (10-6/oC)20-100-Thermal conductivity180 W/mK25-FormingAluminium / Aluminum 6061 alloy can be easily formed and worked in the annealed condition. The standard methods are used to perform bending, stamping, deep drawing, and spinning operations.WeldingAluminium / Aluminum 6061 alloy has excellent weldability. Thinner sections can be welded using gas tungsten arc welding technique. Heavier sections can be welded using gas metal arc welding technique. Alloy 4043 filler wire can be used to achieve good result, but it will affect T 6 properties.Heat TreatmentAluminium / Aluminum 6061 alloy is heat treated at 533°C (990°F) for a sufficient period of time followed by quenching in water. Precipitation hardening process can be performed at 160°C (320°F) for 18 h followed by air cooling. This process is again repeated at 177°C (350°F) for 8 h followed by cooling in air.ForgingAluminium / Aluminum 6061 alloy is forged at 233 to 483°C (750 to 900°F).Hot WorkingAluminium / Aluminum 6061 alloy is hot worked at 260 to 372°C (500 to 700°F).Cold WorkingAluminium / Aluminum 6061 alloy is cold worked in the O temper condition. It can also be cold formed in the T 4 and T 6 tempers.AnnealingAnnealing of Aluminium / Aluminum 6061 alloy can be performed at 775°F for 2 to 3 h followed by controlled cooling at 10 to 260°C (50 to 500°F) per hour, and air cooling.AgingAging of Aluminium / Aluminum 6061 alloy can be performed at 177°C (350°F) for 8 h. It is then cooled in air.[aluminium alloy A96061/A1Mg1SiC /3.3214/H20 ] Surface mill finish , not polished,brushedmirror embossed oxidizedcold-rolledhot-rolled[aluminium alloy A96061/A1Mg1SiC /3.3214/H20 ]Specification:form : Outside Diameter - 0.25mm (0.010") up to 16.00mm (0.625")Wall - 0.05mm (0.002") up to 1.00mm (0.040")Straight Lengths - 1.00mm (0.040") up to 5000.00mm (197")Coils Lengths - 5 Metres to 15 MetresStandard Tolerance- OD &ID +/-0.03mm (0.0012")Wall +/- 10%Tight Tolerance - OD&ID +/- 0.015mm (0.0006")Wall +/-3%Some thin wall tubes up to 25.40 mm (1.000") can be supplied.Temper: 6061-0, 6061-T6, 6061-T651, 6061-T6511Specification: QQ-A-225/8, QQ-A-200/8, AMS 4166, AMS 4117, AMS 4177, AMS 4127, AMS 4128, AMS 4146, AMS 4160, AMS 4161, AMS 4172, AMS 41736061-T6 Cold Finish Bar Per QQ-A-225/8, AMS-QQ-A-225/8, ASTM-B-211, AMS 41176061-T651 Cold Finish Bar Per QQ-A-225/8, AMS-QQ-A-225/8, ASTM-B-211, AMS 41176061-T6 Extruded Bar Per QQ-A-200/8, AMS-QQ-A-200/8, ASTM-B-211, AMS 41506061-T6511 Extruded Bar Per QQ-A-200/8, AMS-QQ-A-200/8, ASTM-B-211, AMS 4173This is our warehouse :This is packaging :
Purchasing Request
Note: Send your purchase request, and we will screen suppliers or manufacturers for you free of charge...