IPDB › China Industry › Metallurgy, Mineral & Energy
China, Chinese Professional Round Bar Steel 4140 Manufacturers Round Bar Steel 4140 Alloy Steel Round Bar1 Industrial Products Supplier Manufacturer Details, price list catalog:
China Industrial Products Supplier Manufacturer List Catalog
Steel ProductsAlloy Steel4140Alloy Steel
Hunan Shunfu Metal Material Co., Ltd.
Preview:
Product Description AISI 4140 G41400 Alloy Steel Round Bar4140 Steel Introduce AISI 4140 steel is a low alloy steel containing chromium, molybdenum, and manganese. It is widely used across numerous industries and is an excellent material choice due to its toughness, high fatigue strength, and abrasion and impact resistance. Not many grades can match the versatility and usefulness of 4140. 4140 Steel Applications This alloy finds many applications as forgings for the aerospace and oil and gas industries, along with myriad uses in the automotive, agricultural and defense industries, Typical uses are forged gears and shafts, spindles, fixtures, jigs and collars. 4140 Steel Chemical Properties GradeCCrMnSiMoSP41400.38-.43%0.80-1.10%0.75-1.0%0.15-0.30%0.15-0.25%0-0.040%0-0.035% 4140 Steel Mechanical Properties PropertiesMetricImperialTensile strength655 MPa95000 psiYield strength415 MPa60200 psiBulk modulus (typical for steel)140 GPa20300 ksiShear modulus (typical for steel)80 GPa11600 ksiElastic modulus190-210 GPa27557-30458 ksiPoisson's ratio0.27-0.300.27-0.30Elongation at break (in 50 mm)25.70%25.70%Hardness, Brinell197197Hardness, Knoop (converted from Brinell hardness)219219Hardness, Rockwell B (converted from Brinell hardness)9292Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only)1313Hardness, Vickers (converted from Brinell hardness)207207Machinability (based on AISI 1212 as 100 machinability)6565 Heat Treatment AISI 4140 alloy steel is heated at 845°C (1550°F) followed by quenching in oil. Before hardening, it can be normalized by heating it at 913°C (1675°F) for a long period of time, followed by air cooling. Forging AISI 4140 alloy steel is forged at 926 to 1205°C (1700 to 2200°F) Hot Working AISI 4140 alloy steel can be hot worked at 816 to 1038°C (1500 to 1900°F) Cold Working AISI 4140 alloy steel can be cold worked using conventional methods in the annealed condition. Annealing AISI 4140 alloy steel is annealed at 872°C (1600°F) followed by slowly cooling in the furnace. Tempering AISI 4140 alloy steel can be tempered at 205 to 649°C (400 to 1200°F) depending upon the desired hardness level. The hardness of the steel can be increased if it has a lower tempering temperature. For example, a tensile strength of 225 ksi can be achieved by tempering at 316°C (600°F), and tensile strength of 130 ksi can be achieved by tempering at 538°C (1000°F). Hardening AISI 4140 alloy steel can be hardened by cold working, or heating and quenching. Machinability AISI 4140 alloy steel has good machinability in the annealed condition. Forming AISI 4140 alloy steel has high ductility. It can be formed using conventional techniques in the annealed condition. It requires more pressure or force for forming because it is tougher than plain carbon steels. Welding AISI 4140 alloy steel can be welded using all conventional techniques. However, the mechanical properties of this steel will be affected if it is welded in the heat-treated condition, and post-weld heat treatment should be performed.
Purchasing Request
Note: Send your purchase request, and we will screen suppliers or manufacturers for you free of charge...